A homogeneous suspension of 300-nanometer LATP powder prepared at 35% solid content. Compared with the 150 nm grade it suits thicker coating layers and higher ceramic filler ratios. Can be used directly in coating processes.

Key Features

Ready dispersion requiring no powder mixing or milling step
300 nm particles suit thicker coatings and higher filler ratios
Low water content with ≤ 0.08% moisture

Technical Specifications

Model	latp300-N35%
Appearance	White uniform suspension
Solid Content	%35.0 ± 2.0
Moisture	≤ %0.08
Particle Size (D50)	0.30 ± 0.06 um

Applications

Thick-film solid electrolyte coating
Composite electrolytes with high ceramic filler ratios
Protective ceramic layers on electrodes

★

Total 0 Comment made

Thank you for your comment. Your comment will be published after it is done.

Comment on you

Thank you for your question. You will be notified by email once your question has been answered.

Click to Ask a Question

No questions have been asked for this product yet.

LATP Solid Electrolyte Slurry - 300 nm (latp300-N35%)

Description

Comments

Question & Answer

Key Features

Technical Specifications

Applications