A silicon oxy-carbon anode material that has undergone a pre-lithiation process. At 1427.2 mAh/g it offers roughly four times the storage capability of graphite. Pre-lithiation compensates in advance for the lithium consumed during SEI formation in the first cycle, delivering a high initial coulombic efficiency of 91.5%.

Key Features

1427.2 mAh/g capacity, roughly four times the storage capability of graphite
High initial coulombic efficiency of 91.5% thanks to pre-lithiation
Tap density of 1.32 g/cm³ supporting high volumetric capacity

Technical Specifications

Particle Size (D10)	4.9 um
Particle Size (D50)	8.2 um
Particle Size (D90)	13.4 um
Tap Density	1.32 g/cm³
Specific Surface Area (SSA)	1.99 m²/g
Capacity	1427.2 mAh/g
Initial Efficiency (ICE)	%91.5